Electrochemically-induced TiO2 incorporation for enhancing corrosion and tribocorrosion resistance of PEO coating on 7075 Al alloy
2018
Abstract 7075 Al alloy was PEO-treated in a silicate based electrolyte containing 3 g l-1 potassium titanyl oxalate using unipolar and bipolar pulsed current waveforms. The coating formed by the bipolar waveform with the wider cathodic pulses showed volcano-like surface morphology with no evidence of large pores at the metal/coating interface. It revealed the highest corrosion performance due to the synergistic effect of TiO2 incorporation and structural/morphological features along with a better passivation behavior indicating no pitting susceptibility. For this coating, the tribocorrosion tests showed no potential drop during sliding under 1 N with the lowest volume loss of 0.022 mm3.
Photoelectrochemical monitoring of rouging and de-rouging on AISI 316L
2017
Electrochemical conditions for inducing rouging on surface of AISI 316L in quasi neutral aqueous solution are studied. Potentiostatic polarization at 0.6 V vs. SSC at pH ∼ 7 allowed growth of colourless passive films with a band gap slightly lower than that estimated for the oxide grown on the SS surface by air exposure due to chromium dissolution. Under stronger anodic polarization (UE = 1.5 V vs. SSC) coloured passive films are formed, mainly constituted by iron oxide according to their band gap (Eg = 2.0 eV). Etching in citric acid at 60 °C results to be effective in removing rouging.